LASER LINE MIRRORS ON UVFS SUBSTRATE
Highly reflective mirrors (>99% reflectivity)
Designed to work at 45° or 0° angle of incidence
Made from UV grade fused silica
Laser line mirrors are dielectric reflectors with an optimized performance at stated laser wavelengths. Our laser mirrors are made from quartz and coated with multilayer dielectric or IBS coating. High polishing quality of the mirror substartes is also important for low wave front distortion, low scattering and high damage threshold.
Dielectric UV fused silica laser line mirors cover a wide range of laser applications in UV, VIS and NIR spectra.
SUBSTRATE
Material
UV grade fused silica
S1 Surface Flatness
λ/10 typical at 633 nm
S1 Surface Quality
20-10 scratch & dig (MIL-PRF-13830B)
S2 Surface Quality
Commercial polish
Diameter Tolerance
+ 0.00 mm, - 0.12 mm
Thickness Tolerance
± 0.25 mm
Wedge
< 3 minutes
Chamfer
0.3 mm at 45° typical
COATING
Technology
Electron beam multilayer dielectric or Ion Beam Sputtering
Adhesion and Durability
Per MIL-C-675A. Insoluble in lab solvents
Clear Aperture
Exceeds central 85% of diameter
Damage Threshold
6 J/cm2, 8 nsec pulse, 1064 nm typical
Coated Surface Flatness
λ/10 at 633 nm over clear aperture
Angle of incidence
0° or 45°
UVFS; ø12.7x3 mm
CODE
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
041-0240-i0
12.7 mm
3 mm
99.0%
0°
244-248 nm
KrF
041-0240
12.7 mm
3 mm
99.0%
45°
244-248 nm
KrF
041-0260
12.7 mm
3 mm
99.0%
45°
262-266 nm
Nd:YAG 4H
041-0260-i0
12.7 mm
3 mm
99.0%
0°
262-266 nm
Nd:YAG 4H
041-0266
12.7 mm
3 mm
99.0%
45°
257-275 nm
Ti:Sa 3H
041-0266-i0
12.7 mm
3 mm
99.0%
0°
257-275 nm
Ti:Sa 3H
041-0325
12.7 mm
3 mm
99.5%
45°
325 nm
HeCd
041-0343
12.7 mm
3 mm
99.5%
45°
333-353 nm
Yb:KGW/KYW 3H
041-0343-i0
12.7 mm
3 mm
99.8%
0°
333-353 nm
Yb:KGW/KYW 3H
041-0350
12.7 mm
3 mm
99.5%
45°
351-361 nm
Nd:YAG 3H
041-0350-i0
12.7 mm
3 mm
99.8%
0°
351-361 nm
Nd:YAG 3H
041-0400
12.7 mm
3 mm
99.5%
45°
380-420 nm
Ti:Sa 2H
041-0400-i0
12.7 mm
3 mm
99.8%
0°
380-420 nm
Ti:Sa 2H
041-0515
12.7 mm
3 mm
99.5%
45°
500-530 nm
Yb:KGW/KYW 2H
041-0515-i0
12.7 mm
3 mm
99.8%
0°
500-530 nm
Yb:KGW/KYW 2H
041-0530
12.7 mm
3 mm
99.5%
45°
527-532 nm
Nd:YAG
041-0530-i0
12.7 mm
3 mm
99.8%
0°
527-532 nm
Nd:YAG
041-0800
12.7 mm
3 mm
99.5%
45°
760-840 nm
Ti:Sa 1H
041-0800-i0
12.7 mm
3 mm
99.8%
0°
760-840 nm
Ti:Sa 1H
041-1030
12.7 mm
3 mm
99.5%
45°
1000-1060 nm
Yb:KGW/KYW 1H
041-1030-i0
12.7 mm
3 mm
99.8%
0°
1000-1060 nm
Yb:KGW/KYW 1H
041-1060
12.7 mm
3 mm
99.5%
45°
1047-1064 nm
Nd:YAG 1H
041-1060-i0
12.7 mm
3 mm
99.8%
0°
1047-1064 nm
Nd:YAG 1H
UVFS; ø12.7 x 6 mm
CODE
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
041-0240T6
12.7 mm
6 mm
99.0%
45°
244-248 nm
KrF
041-0240T6-i0
12.7 mm
6 mm
99.0%
0°
244-248 nm
KrF
041-0260T6
12.7 mm
6 mm
99.0%
45°
262-266 nm
Nd:YAG 4H
041-0260T6-i0
12.7 mm
6 mm
99.0%
0°
262-266 nm
Nd:YAG 4H
041-0266T6
12.7 mm
6 mm
99.0%
45°
257-275 nm
Ti:Sa 3H
041-0266T6-i0
12.7 mm
6 mm
99.0%
0°
257-275 nm
Ti:Sa 3H
041-0343T6
12.7 mm
6 mm
99.5%
45°
333-353 nm
Yb:KGW/KYW 3H
041-0343T6-i0
12.7 mm
6 mm
99.8%
0°
333-353 nm
Yb:KGW/KYW 3H
041-0350T6
12.7 mm
6 mm
99.5%
45°
351-361 nm
Nd:YAG 3H
041-0350T6-i0
12.7 mm
6 mm
99.8%
0°
351-361 nm
Nd:YAG 3H
041-0350T6HHR
12.7 mm
6 mm
99.9%
45°
351-361 nm
Nd:YAG 3H
041-0350T6HHR-i0
12.7 mm
6 mm
99.9%
0°
351-361 nm
Nd:YAG 3H
041-0400T6
12.7 mm
6 mm
99.5%
45°
380-420 nm
Ti:Sa 2H
041-0400T6-i0
12.7 mm
6 mm
99.8%
0°
380-420 nm
Ti:Sa 2H
041-0515T6
12.7 mm
6 mm
99.5%
45°
500-530 nm
Yb:KGW/KYW 2H
041-0515T6-i0
12.7 mm
6 mm
99.8%
0°
500-530 nm
Yb:KGW/KYW 2H
041-0530T6
12.7 mm
6 mm
99.5%
45°
527-532 nm
Nd:YAG
041-0530T6-i0
12.7 mm
6 mm
99.8%
0°
527-532 nm
Nd:YAG
041-0530T6HHR
12.7 mm
6 mm
99.9%
45°
527-532 nm
Nd:YAG
041-0530T6HHR-i0
12.7 mm
6 mm
99.9%
0°
527-532 nm
Nd:YAG
041-0800T6
12.7 mm
6 mm
99.5%
45°
760-840 nm
Ti:Sa 1H
041-0800T6-i0
12.7 mm
6 mm
99.8%
0°
760-840 nm
Ti:Sa 1H
041-0800T6HHR
12.7 mm
6 mm
99.9%
45°
760-840 nm
Ti:Sa 1H
041-0800T6HHR-i0
12.7 mm
6 mm
99.9%
0°
760-840 nm
Ti:Sa 1H
041-1030T6
12.7 mm
6 mm
99.5%
45°
1000-1060 nm
Yb:KGW/KYW 1H
041-1030T6-i0
12.7 mm
6 mm
99.8%
0°
1000-1060 nm
Yb:KGW/KYW 1H
041-1030T6HHR
12.7 mm
6 mm
99.9%
45°
1000-1060 nm
Yb:KGW/KYW 1H
041-1030T6HHR-i0
12.7 mm
6 mm
99.9%
0°
1000-1060 nm
Yb:KGW/KYW 1H
041-1060T6
12.7 mm
6 mm
99.5%
45°
1047-1064 nm
Nd:YAG 1H
041-1060T6-i0
12.7 mm
6 mm
99.8%
0°
1047-1064 nm
Nd:YAG 1H
041-1060T6HHR
12.7 mm
6 mm
99.9%
45°
1047-1064 nm
Nd:YAG 1H
041-1060T6HHR-i0
12.7 mm
6 mm
99.9%
0°
1047-1064 nm
Nd:YAG 1H
UVFS; ø25.4x6 mm
CODE
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
042-0240
25.4 mm
6 mm
99.0%
45°
244-248 nm
KrF
042-0240-i0
25.4 mm
6 mm
99.0%
0°
244-248 nm
KrF
042-0260
25.4 mm
6 mm
99.0%
45°
262-266 nm
Nd:YAG 4H
042-0260-i0
25.4 mm
6 mm
99.0%
0°
262-266 nm
Nd:YAG 4H
042-0266
25.4 mm
6 mm
99.0%
45°
257-275 nm
Ti:Sa 3H
042-0266-i0
25.4 mm
6 mm
99.0%
0°
257-275 nm
Ti:Sa 3H
042-0300-i0
25.4 mm
6 mm
99.2%
0°
308 nm
XeCl
042-0343
25.4 mm
6 mm
99.5%
45°
333-353 nm
Yb:KGW/KYW 3H
042-0343-i0
25.4 mm
6 mm
99.8%
0°
333-353 nm
Yb:KGW/KYW 3H
042-0350
25.4 mm
6 mm
99.5%
45°
351-361 nm
Nd:YAG 3H
042-0350-i0
25.4 mm
6 mm
99.8%
0°
351-361 nm
Nd:YAG 3H
042-0350HHR
25.4 mm
6 mm
99.9%
45°
351-361 nm
Nd:YAG 3H
042-0350HHR-i0
25.4 mm
6 mm
99.9%
0°
351-361 nm
Nd:YAG 3H
042-0400
25.4 mm
6 mm
99.5%
45°
380-420 nm
Ti:Sa 2H
042-0400-i0
25.4 mm
6 mm
99.8%
0°
380-420 nm
Ti:Sa 2H
042-0515
25.4 mm
6 mm
99.5%
45°
500-530 nm
Yb:KGW/KYW 2H
042-0515-i0
25.4 mm
6 mm
99.8%
0°
500-530 nm
Yb:KGW/KYW 2H
042-0530
25.4 mm
6 mm
99.5%
45°
527-532 nm
Nd:YAG 2H
042-0530-i0
25.4 mm
6 mm
99.8%
0°
527-532 nm
Nd:YAG 2H
042-0530HHR
25.4 mm
6 mm
99.9%
45°
527-532 nm
Nd:YAG 2H
042-0530HHR-i0
25.4 mm
6 mm
99.9%
0°
527-532 nm
Nd:YAG 2H
042-0800
25.4 mm
6 mm
99.5%
45°
760-840 nm
Ti:Sa 1H
042-0800-i0
25.4 mm
6 mm
99.8%
0°
760-840 nm
Ti:Sa 1H
042-0800HHR
25.4 mm
6 mm
99.9%
45°
760-840 nm
Ti:Sa 1H
042-0800HHR-i0
25.4 mm
6 mm
99.9%
0°
760-840 nm
Ti:Sa 1H
042-1030
25.4 mm
6 mm
99.5%
45°
1000-1060 nm
Yb:KGW/KYW 1H
042-1030-i0
25.4 mm
6 mm
99.8%
0°
1000-1060 nm
Yb:KGW/KYW 1H
042-1030HHR
25.4 mm
6 mm
99.9%
45°
1000-1060 nm
Yb:KGW/KYW 1H
042-1030HHR-i0
25.4 mm
6 mm
99.9%
0°
1000-1060 nm
Yb:KGW/KYW 1H
042-1060
25.4 mm
6 mm
99.5%
45°
1047-1064 nm
Nd:YAG 1H
042-1060-i0
25.4 mm
6 mm
99.8%
0°
1047-1064 nm
Nd:YAG 1H
042-1060HHR
25.4 mm
6 mm
99.9%
45°
1047-1064 nm
Nd:YAG 1H
042-1060HHR-i0
25.4 mm
6 mm
99.9%
0°
1047-1064 nm
Nd:YAG 1H
UVFS; ø50.8x8 mm
CODE
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
045-0240
50.8 mm
8 mm
99.0%
45°
244-248 nm
KrF
045-0240-i0
50.8 mm
8 mm
99.0%
0°
244-248 nm
KrF
045-0260
50.8 mm
8 mm
99.0%
45°
262-266 nm
Nd:YAG 4H
045-0260-i0
50.8 mm
8 mm
99.0%
0°
262-266 nm
Nd:YAG 4H
045-0266
50.8 mm
8 mm
99.0%
45°
257-275 nm
Ti:Sa 3H
045-0266-i0
50.8 mm
8 mm
99.0%
0°
257-275 nm
Ti:Sa 3H
045-0300
50.8 mm
8 mm
99.2%
45°
308 nm
XeCl
045-0343
50.8 mm
8 mm
99.5%
45°
333-353 nm
Yb:KGW/KYW 3H
045-0343-i0
50.8 mm
8 mm
99.8%
0°
333-353 nm
Yb:KGW/KYW 3H
045-0350
50.8 mm
8 mm
99.5%
45°
351-361 nm
Nd:YAG 3H
045-0350-i0
50.8 mm
8 mm
99.8%
0°
351-361 nm
Nd:YAG 3H
045-0350T12HHR-i0
50.8 mm
12 mm
99.9%
0°
351-361 nm
Nd:YAG 3H
045-0400
50.8 mm
8 mm
99.5%
45°
380-420 nm
Ti:Sa 2H
045-0400-i0
50.8 mm
8 mm
99.8%
0°
380-420 nm
Ti:Sa 2H
045-0515
50.8 mm
8 mm
99.5%
45°
500-530 nm
Yb:KGW/KYW 2H
045-0515-i0
50.8 mm
8 mm
99.8%
0°
500-530 nm
Yb:KGW/KYW 2H
045-0530
50.8 mm
8 mm
99.5%
45°
527-532 nm
Nd:YAG 2H
045-0530-i0
50.8 mm
8 mm
99.8%
0°
527-532 nm
Nd:YAG 2H
045-0530T12HHR
50.8 mm
12 mm
99.9%
45°
527-532 nm
Nd:YAG 2H
045-0530T12HHR-i0
50.8 mm
12 mm
99.9%
0°
527-532 nm
Nd:YAG 2H
045-0800
50.8 mm
8 mm
99.5%
45°
760-840 nm
Ti:Sa 1H
045-0800-i0
50.8 mm
8 mm
99.8%
0°
760-840 nm
Ti:Sa 1H
045-0800T12HHR
50.8 mm
12 mm
99.9%
45°
760-840 nm
Ti:Sa 1H
045-0800T12HHR-i0
50.8 mm
12 mm
99.9%
0°
760-840 nm
Ti:Sa 1H
045-1030
50.8 mm
8 mm
99.5%
45°
1000-1060 nm
Yb:KGW/KYW 1H
045-1030-i0
50.8 mm
8 mm
99.8%
0°
1000-1060 nm
Yb:KGW/KYW 1H
045-1030T12HHR
50.8 mm
12 mm
99.9%
45°
1000-1060 nm
Yb:KGW/KYW 1H
045-1030T12HHR-i0
50.8 mm
12 mm
99.9%
0°
1000-1060 nm
Yb:KGW/KYW 1H
045-1060
50.8 mm
8 mm
99.5%
45°
1047-1064 nm
Nd:YAG 1H
045-1060-i0
50.8 mm
8 mm
99.8%
0°
1047-1064 nm
Nd:YAG 1H
045-1060T12HHR
50.8 mm
12 mm
99.9%
45°
1047-1064 nm
Nd:YAG 1H
UVFS; ø76.2x12.7 mm
CODE
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
047-0266
76.2 mm
12.7 mm
99.0%
45°
257-275 nm
Ti:Sa 3H
047-0266-i0
76.2 mm
12.7 mm
99.0%
0°
257-275 nm
Ti:Sa 3H
047-0343
76.2 mm
12.7 mm
99.5%
45°
333-353 nm
Yb:KGW/KYW 3H
047-0343-i0
76.2 mm
12.7 mm
99.8%
0°
333-353 nm
Yb:KGW/KYW 3H
047-0350
76.2 mm
12.7 mm
99.5%
45°
351-361 nm
Nd:YAG 3H
047-0350-i0
76.2 mm
12.7 mm
99.8%
0°
351-361 nm
Nd:YAG 3H
047-0400
76.2 mm
12.7 mm
99.5%
45°
380-420 nm
Ti:Sa 2H
047-0400-i0
76.2 mm
12.7 mm
99.8%
0°
380-420 nm
Ti:Sa 2H
047-0515
76.2 mm
12.7 mm
99.5%
45°
500-530 nm
Yb:KGW/KYW 2H
047-0515-i0
76.2 mm
12.7 mm
99.8%
0°
500-530 nm
Yb:KGW/KYW 2H
047-0530
76.2 mm
12.7 mm
99.5%
45°
527-532 nm
Nd:YAG 2H
047-0530-i0
76.2 mm
12.7 mm
99.8%
0°
527-532 nm
Nd:YAG 2H
047-0800
76.2 mm
12.7 mm
99.5%
45°
760-840 nm
Ti:Sa 1H
047-0800-i0
76.2 mm
12.7 mm
99.8%
0°
760-840 nm
Ti:Sa 1H
047-1030
76.2 mm
12.7 mm
99.5%
45°
1000-1060 nm
Yb:KGW/KYW 1H
047-1030-i0
76.2 mm
12.7 mm
99.8%
0°
1000-1060 nm
Yb:KGW/KYW 1H
047-1060
76.2 mm
12.7 mm
99.5%
45°
1047-1064 nm
Nd:YAG 1H
047-1060-i0
76.2 mm
12.7 mm
99.8%
0°
1047-1064 nm
Nd:YAG 1H
描述 [描述] Highly reflective (>99% reflectivity) Laser Line Mirrors are made of quartz and coated with multilayer dielectric or IBS coating. Available for UV, VIS and NIR lasers.