DUAL BAND LASER MIRRORS
Dielectric Dual Band Mirrors offer 99.5% reflectivity for the stated wavelengths (fundamental and frequency doubled laser lines or fundamental laser line and its alignment beam).
Highly reflective mirrors (99.5% reflectivity)
Designed to work at 45° or 0° angle of incidence
Made from BK7 glass or UV grade fused silica
Laser Line Mirrors are dielectric reflectors with optimised performance at stated laser wavelengths. Dual band laser mirrors are offered for applications where reflection of two laser lines is needed.
Our laser mirrors are made from BK7 or quartz and coated with dielectric multilayer coating. The achieved high polishing quality is also important for low wave front distortion, low scattering and high damage threshold.
SUBSTRATE
Material
BK7 grade A glass or UV grade fused silica
S1 Surface Flatness
λ/10 typical at 633 nm
S1 Surface Quality
20-10 scratch & dig laser quality
S2 Surface Quality
Commercial polish
Diameter Tolerance
+ 0.00 mm, - 0.12 mm
Thickness Tolerance
± 0.25 mm
Wedge
< 3 minutes
Chamfer
0.3 mm at 45° typical
COATING
Technology
Electron beam multilayer dielectric
Adhesion and Durability
Per MIL-C-675A. Insoluble in lab solvents
Clear Aperture
Exceeds central 85% of diameter
Damage Threshold
BK7 dual line mirrors - 3 J/cm2, 8 nsec pulse, 1064 nm typical
UVFS dual line mirrors - 5 J/cm2, 8 nsec pulse, 1064 nm typicalCoated Surface Flatness
λ/10 at 633 nm over 85% of diameter available
Angle of incidence
0° or 45°
BK7; ø12.7 x 3 mm
CODE
MATERIAL
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
051-4080
BK7
12.7 mm
3 mm
99.5%
45°
390-410+780-820 nm
Ti:Sa 2H+1H
051-4080-i0
BK7
12.7 mm
3 mm
99.5%
0°
390-410+780-820 nm
Ti:Sa 2H+1H
051-5103
BK7
12.7 mm
3 mm
99.5%
45°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
051-5103-i0
BK7
12.7 mm
3 mm
99.5%
0°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
051-5306
BK7
12.7 mm
3 mm
99.5%
45°
532+1064 nm
Nd:YAG 2H+1H
051-5306-i0
BK7
12.7 mm
3 mm
99.5%
0°
532+1064 nm
Nd:YAG 2H+1H
051-6306
BK7
12.7 mm
3 mm
99.5%
45°
633+1064 nm
HeNe:Nd:YAG 1H
051-6306-i0
BK7
12.7 mm
3 mm
99.5%
0°
633+1064 nm
HeNe:Nd:YAG 1H
BK7; ø12.7 x 6 mm
CODE
MATERIAL
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
051-4080T6
BK7
12.7 mm
6 mm
99.5%
45°
390-410+780-820 nm
Ti:Sa 2H+1H
051-4080T6-i0
BK7
12.7 mm
6 mm
99.5%
0°
390-410+780-820 nm
Ti:Sa 2H+1H
051-5103T6
BK7
12.7 mm
6 mm
99.5%
45°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
051-5103T6-i0
BK7
12.7 mm
6 mm
99.5%
0°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
051-5306T6
BK7
12.7 mm
6 mm
99.5%
45°
532+1064 nm
Nd:YAG 2H+1H
051-5306T6-i0
BK7
12.7 mm
6 mm
99.5%
0°
532+1064 nm
Nd:YAG 2H+1H
051-6306T6
BK7
12.7 mm
6 mm
99.5%
45°
633+1064 nm
HeNe:Nd:YAG 1H
051-6306T6-i0
BK7
12.7 mm
6 mm
99.5%
0°
633+1064 nm
HeNe:Nd:YAG 1H
BK7; ø25.4 x 6 mm
CODE
MATERIAL
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
052-4080
BK7
25.4 mm
6 mm
99.5%
45°
390-410+780-820 nm
Ti:Sa 2H+1H
052-4080-i0
BK7
25.4 mm
6 mm
99.5%
0°
390-410+780-820 nm
Ti:Sa 2H+1H
052-5103
BK7
25.4 mm
6 mm
99.5%
45°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
052-5103-i0
BK7
25.4 mm
6 mm
99.5%
0°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
052-5306
BK7
25.4 mm
6 mm
99.5%
45°
532+1064 nm
Nd:YAG 2H+1H
052-5306-i0
BK7
25.4 mm
6 mm
99.5%
0°
532+1064 nm
Nd:YAG 2H+1H
052-6306
BK7
25.4 mm
6 mm
99.5%
45°
633+1064 nm
HeNe:Nd:YAG 1H
052-6306-i0
BK7
25.4 mm
6 mm
99.5%
0°
633+1064 nm
HeNe:Nd:YAG 1H
BK7; ø50.8 x 8 mm
CODE
MATERIAL
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
055-4080
BK7
50.8 mm
8 mm
99.5%
45°
390-410+780-820 nm
Ti:Sa 2H+1H
055-4080-i0
BK7
50.8 mm
8 mm
99.5%
0°
390-410+780-820 nm
Ti:Sa 2H+1H
055-5103
BK7
50.8 mm
8 mm
99.5%
45°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
055-5103-i0
BK7
50.8 mm
8 mm
99.5%
0°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
055-5306
BK7
50.8 mm
8 mm
99.5%
45°
532+1064 nm
Nd:YAG 2H+1H
055-5306-i0
BK7
50.8 mm
8 mm
99.5%
0°
532+1064 nm
Nd:YAG 2H+1H
055-6306
BK7
50.8 mm
8 mm
99.5%
45°
633+1064 nm
HeNe:Nd:YAG 1H
055-6306-i0
BK7
50.8 mm
8 mm
99.5%
0°
633+1064 nm
HeNe:Nd:YAG 1H
BK7; ø76.2 x 12.7 mm
CODE
MATERIAL
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
057-4080
BK7
76.2 mm
12.7 mm
99.5%
45°
390-410+780-820 nm
Ti:Sa 2H+1H
057-4080-i0
BK7
76.2 mm
12.7 mm
99.5%
0°
390-410+780-820 nm
Ti:Sa 2H+1H
057-5103
BK7
76.2 mm
12.7 mm
99.5%
45°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
057-5103-i0
BK7
76.2 mm
12.7 mm
99.5%
0°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
057-5306
BK7
76.2 mm
12.7 mm
99.5%
45°
532+1064 nm
Nd:YAG 2H+1H
057-5306-i0
BK7
76.2 mm
12.7 mm
99.5%
0°
532+1064 nm
Nd:YAG 2H+1H
057-6306
BK7
76.2 mm
12.7 mm
99.5%
45°
633+1064 nm
HeNe:Nd:YAG 1H
057-6306-i0
BK7
76.2 mm
12.7 mm
99.5%
0°
633+1064 nm
HeNe:Nd:YAG 1H
UVFS; ø12.7 x 3 mm
CODE
MATERIAL
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
061-2635
UVFS
12.7 mm
3 mm
99.5%
45°
266+355 nm
Nd:YAG 4H+3H
061-2635-i0
UVFS
12.7 mm
3 mm
99.5%
0°
266+355 nm
Nd:YAG 4H+3H
061-2653
UVFS
12.7 mm
3 mm
99.5%
45°
266+532 nm
Nd:YAG 4H+2H
061-2653-i0
UVFS
12.7 mm
3 mm
99.5%
0°
266+532 nm
Nd:YAG 4H+2H
061-3553
UVFS
12.7 mm
3 mm
99.5%
45°
355+532 nm
Nd:YAG 3H+2H
061-3553-i0
UVFS
12.7 mm
3 mm
99.5%
0°
355+532 nm
Nd:YAG 3H+2H
061-3506
UVFS
12.7 mm
3 mm
99.5%
45°
355+1064 nm
Nd:YAG 3H+1H
061-3506-i0
UVFS
12.7 mm
3 mm
99.5%
0°
355+1064 nm
Nd:YAG 3H+1H
061-4080
UVFS
12.7 mm
3 mm
99.5%
45°
390-410+780-820 nm
Ti:Sa 2H+1H
061-4080-i0
UVFS
12.7 mm
3 mm
99.5%
0°
390-410+780-820 nm
Ti:Sa 2H+1H
061-5103
UVFS
12.7 mm
3 mm
99.5%
45°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
061-5103-i0
UVFS
12.7 mm
3 mm
99.5%
0°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
061-5306
UVFS
12.7 mm
3 mm
99.5%
45°
532+1064 nm
Nd:YAG 2H+1H
061-5306-i0
UVFS
12.7 mm
3 mm
99.5%
0°
532+1064 nm
Nd:YAG 2H+1H
061-6306
UVFS
12.7 mm
3 mm
99.5%
45°
633+1064 nm
HeNe:Nd:YAG 1H
061-6306-i0
UVFS
12.7 mm
3 mm
99.5%
0°
633+1064 nm
HeNe:Nd:YAG 1H
UVFS; ø12.7 x 6 mm
CODE
MATERIAL
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
061-2635T6
UVFS
12.7 mm
6 mm
99.5%
45°
266+355 nm
Nd:YAG 4H+3H
061-2635T6-i0
UVFS
12.7 mm
6 mm
99.5%
0°
266+355 nm
Nd:YAG 4H+3H
061-2653T6
UVFS
12.7 mm
6 mm
99.5%
45°
266+532 nm
Nd:YAG 4H+2H
061-2653T6-i0
UVFS
12.7 mm
6 mm
99.5%
0°
266+532 nm
Nd:YAG 4H+2H
061-3553T6
UVFS
12.7 mm
6 mm
99.5%
45°
355+532 nm
Nd:YAG 3H+2H
061-3553T6-i0
UVFS
12.7 mm
6 mm
99.5%
0°
355+532 nm
Nd:YAG 3H+2H
061-3506T6
UVFS
12.7 mm
6 mm
99.5%
45°
355+1064 nm
Nd:YAG 3H+1H
061-3506T6-i0
UVFS
12.7 mm
6 mm
99.5%
0°
355+1064 nm
Nd:YAG 3H+1H
061-4080T6
UVFS
12.7 mm
6 mm
99.5%
45°
390-410+780-820 nm
Ti:Sa 2H+1H
061-4080T6-i0
UVFS
12.7 mm
6 mm
99.5%
0°
390-410+780-820 nm
Ti:Sa 2H+1H
061-5103T6
UVFS
12.7 mm
6 mm
99.5%
45°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
061-5103T6-i0
UVFS
12.7 mm
6 mm
99.5%
0°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
061-5306T6
UVFS
12.7 mm
6 mm
99.5%
45°
532+1064 nm
Nd:YAG 2H+1H
061-5306T6-i0
UVFS
12.7 mm
6 mm
99.5%
0°
532+1064 nm
Nd:YAG 2H+1H
061-6306T6
UVFS
12.7 mm
6 mm
99.5%
45°
633+1064 nm
HeNe:Nd:YAG 1H
061-6306T6-i0
UVFS
12.7 mm
6 mm
99.5%
0°
633+1064 nm
HeNe:Nd:YAG 1H
UVFS; ø25.4 x 6 mm
CODE
MATERIAL
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
062-2635
UVFS
25.4 mm
6 mm
99.5%
45°
266+355 nm
Nd:YAG 4H+3H
062-2635-i0
UVFS
25.4 mm
6 mm
99.5%
0°
266+355 nm
Nd:YAG 4H+3H
062-2653
UVFS
25.4 mm
6 mm
99.5%
45°
266+532 nm
Nd:YAG 4H+2H
062-2653-i0
UVFS
25.4 mm
6 mm
99.5%
0°
266+532 nm
Nd:YAG 4H+2H
062-3553
UVFS
25.4 mm
6 mm
99.5%
45°
355+532 nm
Nd:YAG 3H+2H
062-3553-i0
UVFS
25.4 mm
6 mm
99.5%
0°
355+532 nm
Nd:YAG 3H+2H
062-3506
UVFS
25.4 mm
6 mm
99.5%
45°
355+1064 nm
Nd:YAG 3H+1H
062-3506-i0
UVFS
25.4 mm
6 mm
99.5%
0°
355+1064 nm
Nd:YAG 3H+1H
062-4080
UVFS
25.4 mm
6 mm
99.5%
45°
390-410+780-820 nm
Ti:Sa 2H+1H
062-4080-i0
UVFS
25.4 mm
6 mm
99.5%
0°
390-410+780-820 nm
Ti:Sa 2H+1H
062-5103
UVFS
25.4 mm
6 mm
99.5%
45°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
062-5103-i0
UVFS
25.4 mm
6 mm
99.5%
0°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
062-5306
UVFS
25.4 mm
6 mm
99.5%
45°
532+1064 nm
Nd:YAG 2H+1H
062-5306-i0
UVFS
25.4 mm
6 mm
99.5%
0°
532+1064 nm
Nd:YAG 2H+1H
062-5306HHR
UVFS
25.4 mm
6 mm
99.9%
45°
532+1064 nm
YAG 1H+2H
062-5306HHR-i0
UVFS
25.4 mm
6 mm
99.9%
0°
532+1064 nm
YAG 1H+2H
062-6306
UVFS
25.4 mm
6 mm
99.5%
45°
633+1064 nm
HeNe:Nd:YAG 1H
062-6306-i0
UVFS
25.4 mm
6 mm
99.5%
0°
633+1064 nm
HeNe:Nd:YAG 1H
UVFS; ø50.8 x 8 mm
CODE
MATERIAL
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
065-2635
UVFS
50.8 mm
8 mm
99.5%
45°
266+355 nm
Nd:YAG 4H+3H
065-2635-i0
UVFS
50.8 mm
8 mm
99.5%
0°
266+355 nm
Nd:YAG 4H+3H
065-2653
UVFS
50.8 mm
8 mm
99.5%
45°
266+532 nm
Nd:YAG 4H+2H
065-2653-i0
UVFS
50.8 mm
8 mm
99.5%
0°
266+532 nm
Nd:YAG 4H+2H
065-3553
UVFS
50.8 mm
8 mm
99.5%
45°
355+532 nm
Nd:YAG 3H+2H
065-3553-i0
UVFS
50.8 mm
8 mm
99.5%
0°
355+532 nm
Nd:YAG 3H+2H
065-3506
UVFS
50.8 mm
8 mm
99.5%
45°
355+1064 nm
Nd:YAG 3H+1H
065-3506-i0
UVFS
50.8 mm
8 mm
99.5%
0°
355+1064 nm
Nd:YAG 3H+1H
065-4080
UVFS
50.8 mm
8 mm
99.5%
45°
390-410+780-820 nm
Ti:Sa 2H+1H
065-4080-i0
UVFS
50.8 mm
8 mm
99.5%
0°
390-410+780-820 nm
Ti:Sa 2H+1H
065-5103
UVFS
50.8 mm
8 mm
99.5%
45°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
065-5103-i0
UVFS
50.8 mm
8 mm
99.5%
0°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
065-5306
UVFS
50.8 mm
8 mm
99.5%
45°
532+1064 nm
Nd:YAG 2H+1H
065-5306-i0
UVFS
50.8 mm
8 mm
99.5%
0°
532+1064 nm
Nd:YAG 2H+1H
065-6306
UVFS
50.8 mm
8 mm
99.5%
45°
633+1064 nm
HeNe:Nd:YAG 1H
065-6306-i0
UVFS
50.8 mm
8 mm
99.5%
0°
633+1064 nm
HeNe:Nd:YAG 1H
UVFS; ø76.2 x 12.7 mm
CODE
MATERIAL
D
ET
R, % (S+P)/2
AOI
WAVELENGTH
APPLICATION
067-2635
UVFS
76.2 mm
12.7 mm
99.5%
45°
266+355 nm
Nd:YAG 4H+3H
067-2635-i0
UVFS
76.2 mm
12.7 mm
99.5%
0°
266+355 nm
Nd:YAG 4H+3H
067-2653
UVFS
76.2 mm
12.7 mm
99.5%
45°
266+532 nm
Nd:YAG 4H+2H
067-2653-i0
UVFS
76.2 mm
12.7 mm
99.5%
0°
266+532 nm
Nd:YAG 4H+2H
067-3506
UVFS
76.2 mm
12.7 mm
99.5%
45°
355+1064 nm
Nd:YAG 3H+1H
067-3506-i0
UVFS
76.2 mm
12.7 mm
99.5%
0°
355+1064 nm
Nd:YAG 3H+1H
067-5103
UVFS
76.2 mm
12.7 mm
99.5%
45°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
067-5103-i0
UVFS
76.2 mm
12.7 mm
99.5%
0°
500-530+1000-1060 nm
Yb:KGW/KYW 2H+1H
067-5306
UVFS
76.2 mm
12.7 mm
99.5%
45°
532+1064 nm
Nd:YAG 2H+1H
067-5306-i0
UVFS
76.2 mm
12.7 mm
99.5%
0°
532+1064 nm
Nd:YAG 2H+1H
067-6306
UVFS
76.2 mm
12.7 mm
99.5%
45°
633+1064 nm
HeNe:Nd:YAG 1H
067-6306-i0
UVFS
76.2 mm
12.7 mm
99.5%
0°
633+1064 nm
HeNe:Nd:YAG 1H
描述 [描述] Dielectric Dual Band Mirrors offer 99.5% reflectivity for the stated wavelengths