HIGH POWER LASER MIRRORS FOR FEMTOSECOND APPLICATIONS
High damage threshold laser mirrors designed for applications with femtosecond lasers. Produced using advanced IBS coating technology.
New ultra high damage threshold laser mirrors are designed for applications with femtosecond lasers. These mirrors are produced using advanced IBS coating technology. Mirrors design wavelengths include 515 nm, 800 nm, 1030 nm and broadband 720-880 nm range with reflection values R>99.8%.
Laser induced damage threshold was measured at mirror design wavelength with 50 fs pulse, 100 Hz under ISO standard 21254-2 1000-on-1 conditions.
Substrate
Material
UV grade fused silica
S1 Surface flatness
λ/10 at 633 nm
S1 Surface quality
20-10 scratch&dig (MIL-PRF-13830B)
S2 Surface quality
Commercial polish
Diameter tolerance
+0.00 mm / -0.12 mm
Thickness tolerance
±0.25 mm
Wedge
< 3 min
Chamfer
0.3 mm at 45° typical
Coating
Technology
Ion Beam Sputtering (IBS)
Adhesion and Durability
Per MIL-C-675A, Insoluble in lab solvents
Clear apterture
Exceeds 85% of diameter
Coated surface flatness
λ/8 at 633 nm over 80% of diameter
Laser Induced Damage Threshold
Measured at design wavelength, 50 fs pulse, 100 Hz
Group Delay Dispersion
|GDD| < 30 fs2
Design wavelength - 343 nm, LIDT @ 343 nm, 200 fs, 100 Hz
CODE
WAVELENGTH
MATERIAL
SIZE
AOI
R, % (S+P)/2
LIDT
041-0343PHR
343 nm
UV FS
ø12.7 x 6 mm
45°
99.8%
>0.4 J/cm²
041-0343PHR-i0
343 nm
UV FS
ø12.7 x 6 mm
0°
99.8%
>0.4 J/cm²
042-0343PHR
343 nm
UV FS
ø25.4 x 6 mm
45°
99.8%
>0.4 J/cm²
042-0343PHR-i0
343 nm
UV FS
ø25.4 x 6 mm
0°
99.8%
>0.4 J/cm²
045-0343PHR
343 nm
UV FS
ø50.8 x 12 mm
45°
99.8%
>0.4 J/cm²
045-0343PHR-i0
343 nm
UV FS
ø50.8 x 12 mm
0°
99.8%
>0.4 J/cm²
Design wavelength - 500-530 nm, LIDT @ 515 nm, 50 fs, 100 Hz
CODE
WAVELENGTH
MATERIAL
SIZE
AOI
R, % (S+P)/2
LIDT
041-0515T6HHR
500-530 nm
UV FS
ø12.7 x 6 mm
45°
99.9%
>0.15 J/cm²
041-0515T6HHR-i0
500-530 nm
UV FS
ø12.7 x 6 mm
0°
99.9%
>0.15 J/cm²
042-0515HHR
500-530 nm
UV FS
ø25.4 x 6 mm
45°
99.9%
>0.15 J/cm²
042-0515HHR-i0
500-530 nm
UV FS
ø25.4 x 6 mm
0°
99.9%
>0.15 J/cm²
045-0515T12HHR
500-530 nm
UV FS
ø50.8 x 12 mm
45°
99.9%
>0.15 J/cm²
045-0515T12HHR-i0
500-530 nm
UV FS
ø50.8 x 12 mm
0°
99.9%
>0.15 J/cm²
Design wavelength - 760-840 nm, LIDT @ 800 nm, 50 fs, 100 Hz
CODE
WAVELENGTH
MATERIAL
SIZE
AOI
R, % (S+P)/2
LIDT
041-0800T6HHR
760-840 nm
UV FS
ø12.7 x 6 mm
45°
99.9%
>0.2 J/cm²
041-0800T6UHHR
760-840 nm
UV FS
ø12.7 x 6 mm
45°
99.9%
>0.3 J/cm²
041-0800T6HHR-i0
760-840 nm
UV FS
ø12.7 x 6 mm
0°
99.9%
>0.2 J/cm²
041-0800T6UHHR-i0
760-840 nm
UV FS
ø12.7 x 6 mm
0°
99.9%
>0.3 J/cm²
041-0800T6HHR-i0-45
760-840 nm
UV FS
ø12.7 x 6 mm
0-45°
99.9%
>0.2 J/cm²
042-0800HHR
760-840 nm
UV FS
ø25.4 x 6 mm
45°
99.9%
>0.2 J/cm²
042-0800UHHR
760-840 nm
UV FS
ø25.4 x 6 mm
45°
99.9%
>0.3 J/cm²
042-0800HHR-i0
760-840 nm
UV FS
ø25.4 x 6 mm
0°
99.9%
>0.2 J/cm²
042-0800UHHR-i0
760-840 nm
UV FS
ø25.4 x 6 mm
0°
99.9%
>0.3 J/cm²
042-0800HHR-i0-45
760-840 nm
UV FS
ø25.4 x 6 mm
0-45°
99.9%
>0.2 J/cm²
045-0800T12HHR
760-840 nm
UV FS
ø50.8 x 12 mm
45°
99.9%
>0.2 J/cm²
045-0800T12UHHR
760-840 nm
UV FS
ø50.8 x 12 mm
45°
99.9%
>0.3 J/cm²
045-0800T12HHR-i0
760-840 nm
UV FS
ø50.8 x 12 mm
0°
99.9%
>0.2 J/cm²
045-0800T12UHHR-i0
760-840 nm
UV FS
ø50.8 x 12 mm
0°
99.9%
>0.3 J/cm²
045-0800T12HHR-i0-45
760-840 nm
UV FS
ø50.8 x 12 mm
0-45°
99.9%
>0.2 J/cm²
Design wavelength - 720-880 nm, LIDT @ 800 nm, 50 fs, 100 Hz
CODE
WAVELENGTH
MATERIAL
SIZE
AOI
R, % (S+P)/2
LIDT
081-7288HHR
720-880 nm
UV FS
ø12.7 x 6 mm
45°
99.8%
>0.15 J/cm²
081-7288HHR-i0
720-880 nm
UV FS
ø12.7 x 6 mm
0°
99.9%
>0.15 J/cm²
082-7288HHR
720-880 nm
UV FS
ø25.4 x 6 mm
45°
99.8%
>0.15 J/cm²
082-7288HHR-i0
720-880 nm
UV FS
ø25.4 x 6 mm
0°
99.9%
>0.15 J/cm²
085-7288T12HHR
720-880 nm
UV FS
ø50.8 x 12 mm
45°
99.8%
>0.15 J/cm²
085-7288T12HHR-i0
720-880 nm
UV FS
ø50.8 x 12 mm
0°
99.9%
>0.15 J/cm²
087-7288HHR
720-880 nm
UV FS
ø76.2 x 15 mm
45°
99.8%
>0.15 J/cm²
087-7288HHR-i0
720-880 nm
UV FS
ø76.2 x 15 mm
0°
99.9%
>0.15 J/cm²
Design wavelength - 1000-1060 nm, LIDT @ 1030 nm, 50 fs, 100 Hz
CODE
WAVELENGTH
MATERIAL
SIZE
AOI
R, % (S+P)/2
LIDT
041-1030T6HHR
1000-1060 nm
UV FS
ø12.7 x 6 mm
45°
99.9%
>0.4 J/cm²
041-1030T6HHR-i0
1000-1060 nm
UV FS
ø12.7 x 6 mm
0°
99.9%
>0.4 J/cm²
042-1030HHR
1000-1060 nm
UV FS
ø25.4 x 6 mm
45°
99.9%
>0.4 J/cm²
042-1030HHR-i0
1000-1060 nm
UV FS
ø25.4 x 6 mm
0°
99.9%
>0.4 J/cm²
045-1030T12HHR
1000-1060 nm
UV FS
ø50.8 x 12 mm
45°
99.9%
>0.4 J/cm²
045-1030T12HHR-i0
1000-1060 nm
UV FS
ø50.8 x 12 mm
0°
99.9%
>0.4 J/cm²
Design wavelength - 1400-1700 nm , LIDT @ 1550 nm, 50 fs, 100 Hz
CODE
WAVELENGTH
MATERIAL
SIZE
AOI
R, % (S+P)/2
LIDT
i081-1417
1400-1700 nm
UV FS
ø12.7 x 6 mm
45°
99.8%
>0.3 J/cm²
081-1417-i0
1400-1700 nm
UV FS
ø12.7 x 6 mm
0°
99.8%
>0.3 J/cm²
082-1417
1400-1700 nm
UV FS
ø25.4 x 6 mm
45°
99.8%
>0.3 J/cm²
085-1417
1400-1700 nm
UV FS
ø50.8 x 12 mm
45°
99.8%
>0.3 J/cm²
085-1417-i0
1400-1700 nm
UV FS
ø50.8 x 12 mm
0°
99.8%
>0.3 J/cm²
Design wavelength - 1900-2120 nm , LIDT @ 2000 nm, 50 fs, 100 Hz
CODE
WAVELENGTH
MATERIAL
SIZE
AOI
R, % (S+P)/2
LIDT
081-1921
1900-2120 nm
UV FS
ø12.7 x 6 mm
45°
99.8%
>0.4 J/cm²
081-1921-i0
1900-2120 nm
UV FS
ø12.7 x 6 mm
0°
99.8%
>0.4 J/cm²
082-1921
1900-2120 nm
UV FS
ø25.4 x 6 mm
45°
99.8%
>0.4 J/cm²
082-1921-i0
1900-2120 nm
UV FS
ø25.4 x 6 mm
0°
99.8%
>0.4 J/cm²
085-1921
1900-2120 nm
UV FS
ø50.8 x 12 mm
45°
99.8%
>0.4 J/cm²
085-1921-i0
1900-2120 nm
UV FS
ø50.8 x 12 mm
0°
99.8%
>0.4 J/cm²
描述 [描述] High damage threshold laser mirrors designed for applications with femtosecond lasers. Produced using advanced IBS coating technology.